基于激光闪光法的立式热扩散率测量装置研究

介绍了基于激光闪光法的立式热扩散率测量装置,利用脉冲激光对样品进行均匀加热,使样品内部产生一维热流,并通过红外探测器测量样品温升信号,采用立式真空加热炉控制测量温度环境,实现室温至1600℃的热扩散率测量。用该装置测量厚度为1. 1 mm,直径为10 mm的不锈钢样品,测量结果与PTB参考数据的偏差小于1%。     

Mechanical properties of continuous bamboo fiber-reinforced biobased polyamide 11 composites

This study is devoted to the analysis of the properties of continuous bamboo fiber (BF)-reinforced polyamide 11 (PA 11) composites. The SEM observations highlighted continuity between BFs and the polymeric matrix showing a high density of hydrogen bonds. The comparative calorimetric study of the matrix and its composites showed that the crystallinity of PA 11 was not modified by the presence of bamboo fibers. The physical aging observed in PA 11 is no more observed in composites due to physical interactions between PA 11 and BFs. The mechanical properties were investigated by tensile strength and dynamic mechanical analysis. The introduction of BFs enhanced Young's modulus of the matrix by a factor of 10. The presence of BFs also improved the storage shear modulus G′ over the whole temperature range. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47623.     

QKD系统中基于EA电路的诱骗态实现

使用诱骗态量子秘钥方案可以解决因光子数分离攻击而导致的安全漏洞,保证了长距离量子通信的安全。本文介绍了量子通信的相关原理,通过对电吸收调制电路和激光器驱动电路的设计,精确控制产生了1550 nm波段的窄脉冲,经过内部调制成功制备诱骗态光脉冲,其强度约为信号态光脉冲的三分之一,因激光器的同一性而具有一致的光学特征从而避免了时频窃听,并具有强度可调的优点。     

靶面激光光斑尺寸原位测量的研究

提供了一种简便易行的靶面激光光斑尺寸原位测量的方法。从高斯光束的横向光强分布特性出发,建立了激光烧蚀斑半径与辐照激光能量、光斑尺寸、烧蚀阈值间的关系式,模拟分析发现辐照激光光斑尺寸对烧蚀斑半径随辐照能量变化曲线有较大影响。对于脉宽为2 ms,波长为1064 nm的激光,实验测量了不同能量激光辐照下相纸烧蚀斑半径,并用推导出的关系式拟合测量数据,获得了靶面处光斑尺寸和样品烧蚀阈值。同时,也测量了不同位置处的光斑尺寸和样品烧蚀阈值,对高斯光束束腰位置和样品烧蚀阈值的光斑尺寸效应进行了验证。研究结果表明该技术结果可靠,简单高效。该技术可以为高能激光与固体物质相互作用的基础研究和激光加工等应用领域中实现简单方便地测量靶面光斑尺寸提供帮助。     

磁场环境下铝电解熔融铝液成分激光诱导击穿光谱原位测量分析

铝电解车间具有高温、强磁、多粉尘等环境特点,当前生产过程中熔融原铝的成分检测主要是人工取样然后离线分析,化验过程及结果具有较大的滞后性,故将激光诱导击穿光谱(LIBS)技术应用于铝电解车间铝液成分原位、实时测量具有重要意义。实验采用Nd:YAG脉冲激光器,多通道光纤光谱仪和电感耦合器件(CCD)探测器组成的激光诱导击穿光谱测量系统对电流为400kA电解槽中熔融铝液的主要成分铁、硅进行了探测,对原铝中部分元素的特征谱线进行了归属分析。考察了激光能量在磁场环境下的衰减变化及谱线梯度变迁规律,结果表明,距离电解槽边缘约2m处激光能量衰减达最大。分析了磁场对测试系统的影响,并建立了定标曲线,铁和硅两种元素按照内标法建立的定标曲线拟合度分别为93.50%和97.10%,采用该模型进行了测试实验,并用国标GB/T 7999—2015中光电直读发射光谱(OES)测试的相关指标验证测试结果的重复性与允许差。实验证明,LIBS技术在电解铝行业在线检测方面具有较好的应用前景,但是测试的稳定性与重复性也是面临的一个重要问题。     

Pump laser induced photodarkening in ZrO2-doped Yb:Y2O3 laser ceramics

5 at.% Yb:Y₂O₃ transparent ceramics were fabricated using vacuum sintering plus HIP. The ceramics doped with 1 at.% ZrO₂ as the sintering additive were densified at 1700 °C in vacuum followed by HIPing at 1775 °C, while those without sintering additives were densified at 1520 °C in vacuum followed by HIPing at 1450 °C. After sintering, both ceramics had relatively high in-line transmittance. However, during laser experiments, the ZrO₂-doped Yb:Y₂O₃ (Zr-YbY) ceramics were photodarkened when irradiated by 940 nm pump light. The discoloration might be attributed to the formation of Zr³⁺ color centers during lasing. In contrast, no photodarkening effect was detected in the pure Yb:Y₂O₃ ceramics without sintering additives (P-YbY). The P-YbY ceramics exhibited much higher lasing efficiency (17%) than the Zr-YbY ceramics (9%). To our best knowledge, it is the first time that the photodarkening effect was detected in rare-earth doped sesquioxide laser ceramics.     

高功率光纤激光器光纤器件封装应力影响研究

高功率激光器无源器件制作过程中封装不当引入的应力,会导致信号光光束质量劣化和光纤温升,为了解决此问题,理论分析了光纤形变对信号光模式分布的影响,利用有限元方法建立包层光导致光纤发热模型,实验研究了不同封装方式对光纤发热情况和信号光光束质量的影响。实验表明,应力导致的光纤形变会造成信号光M2值在受力方向上略微变小而其垂直方向上变大,在输出100 W信号光时,施加应力导致的M2值的变化最高为0.39,与仿真结果相符。在光纤温升方面,相比于使用硬质胶水带来的12 ℃温升,使用硅橡胶封装的剥离器将温升控制在5 ℃以内,且其封装应力引入的M2值的变化在0.05以内。     

一种基于LTCC基板的数字光收发模块设计

首先介绍低温共烧陶瓷(LTCC)技术和数字光收发模块,阐述LTCC的技术特点、工艺流程以及它相较于传统PCB电路基板的优势,解释了数字光收发模块的通信原理和工作方式;其次,提出了一种基于LTCC电路基板的数字光收发模块的设计方案,详细介绍了该光模块的主要构成和实现方法,包括电路设计和关键器件的比较和选取;最后,通过对该方案所述的数字光收发模块的样件进行关键指标和性能测试,验证了该设计方案的可行性。